For Use at Low-temperature
When applying conveyor chains at low-temperature this kind of as in a refrigerator or in the cold ambiance, the following conditions may come about.
1) Very low temperature brittleness
Normally, a materials is embrittled at low-temperature and shock resistance is lowered. This phenomenon is called low-temperature brittleness, as well as degree of embrittlement differs from material to material.
The service limit of a conveyor chain depends on its specifications.
two)Influence of freezing
At low-temperature, bending failure, roller rotation failure, repairing of chain, and so on. could possibly be brought about from the freezing of penetrated water or deposited frost from the clearance among pins and bushings, bushings and rollers or inner plates and outer plates. These ailments cause an overload to act within the chain and drive, diminishing the life of the chain.
To avoid freezing, generally, it’s encouraged to fill the clearances using a low-temperature lubricant appropriate on the services temperature to avoid water, frost, etc. from penetrating the respective portions from the chain. For lubrication, a silicon primarily based grease is advisable.
For Use at High-temperature
Chains power is diminished by high-temperature atmosphere, direct conveying of high-temperature loads, or radiated heat, and so forth. The services restrict at high-temperature depends not within the temperature on the support environment however the temperature and material in the chain physique.
Following situations could occur when chains are used at high-temperature:
1) High temperature brittleness and fracture by lowered hardness of heat taken care of material
2) Brittleness brought on by carbide precipitation
3) Abnormal put on by scale
4) Fatigue fracture induced by repeated thermal shock (cooling and expansion)
five) Abnormal put on on account of an increase from the coefficient of friction
six) Creep fracture
7) Fracture on account of thermal fatigue of welded spot
8) Effects triggered by thermal expansion
?Stiff back links and rotation failure as a result of decreased clearance ?Fatigue fracture 
as a consequence of lowered fitting force
9）Lubrication failure and stiff links as a result of deterioration and carbonization of lubricating oil
Grease excellent in heat resistance contain those according to silicon, graphite or molybdenum disulfide.
For use at high-temperature, high-temperature resistance bearings and stainless steel bearings are encouraged.